Refractory High Alumina Super Duty Fire Brick for Furnace Lining

• Feature: Long Time Materials, Instant Materials
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Brick, Dense Brick
• Model NO.: YUFENGREC-A36, YUFENGREC-A40, YUFENGREC-A42
• Size(Shapes): Straights, Arch, Wedge, Soaps, Splits...
• Bulk Density: 2150 Kg/M3 - 3200 Kg/M3
• Type: High Alumina and Fireclay
• Material: Super Quality Bauxite and Flint Clay
• Transport Package: Export Standar Wooden Pallet
• Specification: ASTM Standard
• Trademark: YUFENGREC
• Origin: China
• HS Code: 69022000
• Production Capacity: 30000 Tons /Year

Product Description

YUFENGREC^® Fireclay Brick & High Alumina Brick  are made of high-grade Flint Clay,Chamotte ,High Alumina Bauxite  with alumina content from 36% to 85% , producing by drying pressing and high fired .

YUFENGREC^® Mullite Bricks based on synthetic fused Mullite  and sintered Mullite  shaped by high pressure presses or casting process as per different applications  and fired in high temperature  furnaces  . Mullite Brick features with good thermal properties and adequate erosion and corrosion  resistance  ,which is widely used to hot end of regenerative  chambers  of glass melter , superstructure of the furnace  .

YUFENGREC^® Andalusite Bricks is made by  non-contaminated andalusite from natural sources as the raw material ,shaped by hydraulic high pressure presses .During the production processing, the bricks is strictly controlled with the reasonable particle size of the raw materials ,adopt new process , multi-stage ingredients, matrix homogenization, and determines the best calcination temperature  etc.,  to achieve  high quality level  to  meet the use of different parts of blast furnace and hot blast stove and different working environments

 

Classification : ASTM C-27

 

Method of Manufacturer: Dry Pressing

Key Features 

* High Strength

* Lower Shrinkage

* Excellent Alkalis Resistant

* Good resistant to Thermal Shock

* High Refractoriness under load

Typical Applications

* Carbon Baking pit furnace  flue-walls and head walls

* Air Heaters

* Combustion Chamber .

* Boiler

* Stack

* Blast Furnace

* Hot Blast Stove

* Cement Rotary Kiln

* Glass Furnace

* kinds of high temperature  industry furnace

 

Dimensions

* 230 x 114 x 64 mm

* 230 x 114 x 76 mm
* 250 x 124 x 64 mm

* 220 x 110 x 60  mm

* Customized production for bricks with special dimension  is available

 

Packing   

* In export standard wooden pallet
 

Typical Technical Data

* Fireclay Brick 

Item	Fireclay Brick
	High Duty Fireclay Brick	Super Duty Fireclay Brick	High Fired ,Super Duty, Dry Press Fireclay Brick
Al2O3	≥36 %	≥42 %	≥42.1
Fe2O3	≤2.5%	≤2.5%	≤2.0
Pyrometric Cone Equivalent       Orton Standard Cones     Temperature Equivalent	32               1717ºC	34                                              1753ºC	34                                              1753ºC
Bulk Density	≥2.15	≥2.20	≥2.29
Apparent Porosity	22-24%	22-24%	17-19%
Cold crushing strength	≥25	≥35	≥42
Hot Load Test Deformation at 1350ºC	1%	-0.2 to -0.7%	≥05-0.7%
Permanent Linear Change at 1400 ºC	-0%	-0%	0%

* High Alumina Brick 

Item	High Alumina Brick
	SK36	SK37	SK38	SK40
Al2O3	55%	60	70	79.6
Fe2O3	2.0%	2.0%	2.0%	2.0%
Pyrometric Cone Equivalent           Orton Standard Cones	35	37	38	40
Bulk Density	2.30 g/cm3	2.35g/cm3	2.45 g/cm3	2.60 g/cm3
Cold crushing strength	31 MPA	44 MPA	48 MPA	55 MPA
Apparent Porosity	22%	22%	21%	20%
Permanent Linear Change at 1600 ºC	+0.1 to +2.5%	+1.5 to +2.5%	+2.0 to +4.0%	+1.0 to +2.0%

* Special High Quality Fireclay Brick with Low Porosity  

Item	Unit	Special High Quality FireClay Brick  With Low Porosity
		YUFENG-DN11	YUFENG-DN14	YUFENG-DN17
Al2O3	%	≥47	≥45	≥42
Fe2O3	%	≤1.20	≤1.5	≤1.80
Bulk Density	g/cm^3	≥2.40	≥2.34	≥2.26
Apparent Porosity	%	≤11	≤14	≤17
Cold crushing strength	MPa	≥80	≥65	≥50
Permanent Linear Change at 1400 ºCx 2h	%	-	+0.1 to -0.2%	+0.1 to -0.2%
at 1500 ºCx 2h		+0.1 to -0.2%	-	-
Refractoriness Under Load 0.2 MPa T0.5	T0.5 /ºC	≥1520	≥1470	≥1430

* Andalusite Brick 

Item		Unit	Andalusite Brick
			YUFENGREC-A-55	YUFENGREC-A-60
Al2O3		%	≥55	≥60
Fe2O3		%	≤1.0%	≤1.5%
Bulk Density		g/cm^3	≥2.45	≥2.50
Apparent Porosity		%	22	22
Cold crushing strength		MPa	≥40	≥45
Permanent Linear Change	1500 ºCx 3h	%	+/- 0.2	+/- 0.2
Refractoriness Under Load     (2kg/cm^2,T2)		ºC	1450	1500

* Mullite Brick 

Item	Unit	Casting Corundum-Mullite		Sintered Mullite				Fused Mullite	Sintered Corundum -Mullite		Casting Mullite
		CCM85	CCM80	SM65	SM70	SM75	SM80	FM75	SCM85	SCM80	M70
Al2O3	%	85	80	64	68	74	78	72	85	80	69
Fe2O3	%	0.5	0.5	1.2	1.2	0.8	0.6	0.5	0.5	0.5	0.8
Refractoriness	ºC	1810	1810	1790	1790	1790	1810	1810	1810	1810	1790
Bulk Density	g/cm^3	21	22	18	20	18	18	18	18	18	20
Apparent Porosity	%	2.75	2.65	2.45	2.50	2.60	2.75	2.65	2.90	2.80	2.50
Cold Crushing Strength	MPa	60	60	55	60	65	70	70	80	70	60
Refractoriness Under Load	ºC	1700	1650	1560	1580	1650	1700	1700	1700	1700	1650
Permanet Linear Change 1400 ºC x 2h	%	---	---	---	---	---	---	---	---	---	---
1500ºC x 2 h		+  0.1          -  0.2	+  0.1          -  0.2	+  0.1             -  0.4	+  0.1          -  0.3	+  0.1          -  0.2	+  0.1          -  0.2	+  0.1              -  0.1	+  0.1              -  0.1	+  0.1              -  0.1	+  0.1              -  0.2

Producing Procedure 

QC Inspection

Applications 